Raw Material Alloy 440C UNS S44000 DIN1.4125 SUS 440C Black Polished 25mm Stainless Steel Round Bar
Stainless steels are high-alloy steels which have high corrosion resistance compared to other steels due to the presence of large amounts of chromium. Based on their crystalline structure, they are divided into three types such as ferritic, austenitic, and martensitic steels. Another group of stainless steels are precipitation-hardened steels. They are a combination of martensitic and austenitic steels.
Grade 440C stainless steel is a high carbon martensitic stainless steel. It has high strength, moderate corrosion resistance, and good hardness and wear resistance. Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys. Its very high carbon content is responsible for these characteristics, which make 440C particularly suited to such applications as ball bearings and valve parts.
Typical applications include:
UNS: ASTM/ASTE S44000
DIN: 1.4125
| Name | stainless steel round bar | material | 440C |
| OD size | 10-250mm | Length | 6m |
| surface | polished / black | standard | ASTM A276 |
Supply Range for 440C Stainless Steel
440C steel round bar: diameter 1mm～400mm
440C stainless plate: 0.1-100 thickness x 500-2000mm width x 1000-6000mm length
Other steel shape, like 440c steel sheet, 440C coil, flat bar and customized sizes are available against request
| Country | USA | BS & DIN | Japan |
| Standard | ASTM A276 | EN 10088 | JIS G4303 |
| Grades | S44004/440C | X105CrMo17/1.4125 | SUS440C |
| Standard | Grade | C | Mn | P | S | Si | Cr | Mo |
| ASTM A276 | S44004/440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
| EN10088 | X105CrMo17/1.4125 | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | 0.40-0.80 |
| JIS G4303 | SUS 440C | 0.95-1.20 | ≦1.00 | ≦0.04 | ≦0.03 | ≦1.00 | 16.0-18.0 | ≦0.75 |
| Tempering Temperature (°C) | Tensile Strength (MPa) | Yield Strength 0.2% Proof (MPa) | Elongation (% in 50mm) | Hardness Rockwell (HRC) | Impact Charpy V (J) |
| Annealed* | 758 | 448 | 14 | 269HB max# | – |
| 204 | 2030 | 1900 | 4 | 59 | 9 |
| 260 | 1960 | 1830 | 4 | 57 | 9 |
| 316 | 1860 | 1740 | 4 | 56 | 9 |
| 371 | 1790 | 1660 | 4 | 56 | 9 |
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (mm/m/°C) | Thermal Conductivity(W/m.K) | Specific Heat | Electrical Resistivity (nW.m) | |||
| 0-100°C | 0-200°C | 0-600°C | at 100°C | at 500°C | 0-100°C (J/kg.K) | ||||
| 440 C | 7650 | 200 | 10.1 | 10.3 | 11.7 | 24.2 | – | 460 | 600 |
Preheat to 760oC – 820oC, then heat slowly and uniformly to 1050oC – 1150oC, hold until temperature is uniform throughout the 440c steel section and commence forging immediately. Do not overheat 440c stainless steel as this can cause a loss of toughness and ductility. Do not forge below 900oC. Finished forgings of SS 440c should be cooled slowly in a furnace, warm dry lime or ashes to room temperature and annealed immediately. Air cooling after forging may cause cracking of steel 440c.
ASTM Grade 440C stainless steel can be machined well, with all operations such as turning and drilling etc., in the annealed condition. Because of 440C SS high carbon content it machines somewhat like high-speed steel. Because chips are tough and stringy, chip curlers and breakers are important.
As heat treated, the 440 steel series are difficult to machine because of their high hardness. For parts that require extensive machining, the free-machining versions, Type 440F or Type 440F Se, offer improved machining properties.